TEROSON MS 9220 BK CR3 10ML M/L
TEROSON MS 9220 BK CR3 10ML M/L
Henkel
Teroson MS 9220 Flexible Sealant
Colour : Black
Teroson MS 9220 is a one component adhesive with high sag resistance, based on MS-Polymer.
Characteristics:
Cures by reaction with humidity to an elastic product
The skin formation and curing times are dependent on humidity and temperature
The curing time also depends on joint depth
By increasing the temperature and humidity, the reaction time can be reduced
Free of solvents, isocyanates, silicones and PVC
Has only a weak odour (after curing it is odourless)
Good adhesion to many substrates
Good resistance to UV-light
Application:
Vehicle body manufacture
Bus manufacture
Vehicle body build-ups
Caravan
Ship and boat building
Technical Specifications:
Odour: odourless
Consistancy: thixotropic paste
Density: approx. 1,4 g/cm³
Skin formation time: approx. 6 min
Tack-free time: approx. 20 to 30 min
Cure rate: approx. 3,5 mm/24 h
Shore-A-hardness (DIN 53505): approx. 60
Tensile strength (acc. to DIN 53504): approx. 3,3 MPa
Tensile shear strength (DIN EN 1465): 4,4 MPa
Substrates: painted sheet metal
Layer thickness: 0,2 mm
Cross head speed: 10 mm/min
Volume change (acc. to DIN 52451): < 2%
Application temperature: +15°C to +35°C
In service temperature range: -40°C to +100°C
Short exposure (up to 1 h): +120°C
Teroson MS 9220 Flexible Sealant
Colour : Black
Teroson MS 9220 is a one component adhesive with high sag resistance, based on MS-Polymer.
Characteristics:
- Cures by reaction with humidity to an elastic product
- The skin formation and curing times are dependent on humidity and temperature
- The curing time also depends on joint depth
- By increasing the temperature and humidity, the reaction time can be reduced
- Free of solvents, isocyanates, silicones and PVC
- Has only a weak odour (after curing it is odourless)
- Good adhesion to many substrates
- Good resistance to UV-light
Application:
- Vehicle body manufacture
- Bus manufacture
- Vehicle body build-ups
- Caravan
- Ship and boat building
Technical Specifications:
- Odour: odourless
- Consistancy: thixotropic paste
- Density: approx. 1,4 g/cm³
- Skin formation time: approx. 6 min
- Tack-free time: approx. 20 to 30 min
- Cure rate: approx. 3,5 mm/24 h
- Shore-A-hardness (DIN 53505): approx. 60
- Tensile strength (acc. to DIN 53504): approx. 3,3 MPa
- Tensile shear strength (DIN EN 1465): 4,4 MPa
- Substrates: painted sheet metal
- Layer thickness: 0,2 mm
- Cross head speed: 10 mm/min
- Volume change (acc. to DIN 52451): < 2%
- Application temperature: +15°C to +35°C
- In service temperature range: -40°C to +100°C
- Short exposure (up to 1 h): +120°C
Teroson MS 9220 Flexible Sealant
Colour : Black Teroson MS 9220 is a one component adhesive with high sag resistance, based on MS-Polymer. Characteristics:
- Cures by reaction with humidity to an elastic product
- The skin formation and curing times are dependent on humidity and temperature
- The curing time also depends on joint depth
- By increasing the temperature and humidity, the reaction time can be reduced
- Free of solvents, isocyanates, silicones and PVC
- Has only a weak odour (after curing it is odourless)
- Good adhesion to many substrates
- Good resistance to UV-light
- Vehicle body manufacture
- Bus manufacture
- Vehicle body build-ups
- Caravan
- Ship and boat building
- Odour: odourless
- Consistancy: thixotropic paste
- Density: approx. 1,4 g/cm³
- Skin formation time: approx. 6 min
- Tack-free time: approx. 20 to 30 min
- Cure rate: approx. 3,5 mm/24 h
- Shore-A-hardness (DIN 53505): approx. 60
- Tensile strength (acc. to DIN 53504): approx. 3,3 MPa
- Tensile shear strength (DIN EN 1465): 4,4 MPa
- Substrates: painted sheet metal
- Layer thickness: 0,2 mm
- Cross head speed: 10 mm/min
- Volume change (acc. to DIN 52451): < 2%
- Application temperature: +15°C to +35°C
- In service temperature range: -40°C to +100°C
- Short exposure (up to 1 h): +120°C